Nexa3D KeySplint Soft Resin 5kg For NX
$2,502
KeySplint Soft® device is indicated for the fabrication of orthodontic and dental appliances such as bite planes, mouthguards, nightguards, snoring appliances, splints, and repositioners.
Choose your color: Light Violet or Translucent.
Details
| Weight | 12 lbs |
|---|---|
| Dimensions | 9 × 6 × 10 in |
| Brand | |
| Available colors | Light Violet, Translucent |
| Weight | 5 kg |
| Country of origin | USA |
| Platform | NX |
Description
Unique Features
- Biocompatible
- Strong
- Flexible
- Easy to polish
- Easily Cleaned
PHYSICAL AND MECHANICAL PROPERTIES
| Elongation at Break | ASTM D638 | 110% |
| Flexural Modulus | ASTM D790 | 1100 MPa |
| Flexural Strength | ASTM D790 | 44 MPa |
| Flexural Modulus | ISO 20795-2 | 135 MPa |
| Flexural Strength | ISO 20795-2 | 2.6 MPa |
| Shore Hardness (0s, 3s) D scale | ASTM D2240 | 80 |
| HDT @0.45 MPa | ASTM D648 | 32°C |
| Sorption | ISO 20795-2 | <18 μg/mm3 |
| Solubility | ISO 20795-2 | <4.8 μg/mm3 |
| Free Monomer Extraction | <2.2% | |
| Cytotoxicity | ISO 10993 | Pass |
| Irritation | ISO 10993 | Pass |
| Sensitization | ISO 10993 | Pass |
downloads
Related products
-
Nexa3D xCE-White Resin 5kg
$1,328High performance polymer for producing end-use plastic parts and injection molding tools in minutes.Nexa3D xCE-White Resin 5kg
High performance polymer for producing end-use plastic parts and injection molding tools in minutes. xCE White is the fastest single cure polymer boasting higher flexural strength compared to those typically achieved only in dual cure cyanate ester resins, and has excellent isotropic properties that exhibit long-term environmental stability.
$1,328 Add to cart -
Alumina Toughened Zirconia 3D Printing Paste
OXIDE CERAMICS Alumina Toughened Zirconia, known for their biocompatibility and their resistance toAlumina Toughened Zirconia 3D Printing Paste
OXIDE CERAMICS
Alumina Toughened Zirconia, known for their biocompatibility and their resistance to wear and thermal shock, are recommended for biomedical and industry applications.
The ceramic ATZ combines both Alumina (20%) and Zirconia (80%) ceramics in one. The mix of these two combined offers several properties.