KS158A Transparent UV SLA Resin
KS158T UV SLA Resin is an optically transparent SLA resin ideally applicable for parts with acrylic appearance and light components.
Download KS158A Transparent SLA 3D printing resin brochure
Download
Details
Brand | |
---|---|
Country of origin | China |
Appearance | Transparent |
Density | 1.12g/cm3 at 25 ℃ |
Viscosity | 408 cps at 26 ℃ |
Dp | 0.0071in / 0.18mm |
Ec | 6.7 mJ/c㎡ |
Building layer thickness | 0.0039in / 0.01mm |
Hardness, Shore D | 72-78 (ASTM D 2240) |
Flexural modulus, Mpa | 2,680-2,775 (ASTM D 790) |
Flexural strength, Mpa | 65- 75 (ASTM D 790) |
Tensile modulus, MPa | 2,170-2,385 (ASTM D 638) |
Tensile strength, MPa | 25-30 (ASTM D 638) |
Elongation at break | 12 -20 % (ASTM D 638) |
Impact strength, notched lzod, J/m | 58 – 70 (ASTM D 256) |
Heat deflection temperature, ℃ | 50-60 (ASTM D 648 at 66 PSI) |
Glass transition, Tg,℃ | 55-70 (DMA,E”peak) |
Density, g/cm3 | 1.14-1.16 (UV Postcure) |